It is very easy to cause concrete cracking if the construction or maintenance are not done correctly. What are then the five main causes of cracking concrete?
1. The cement proportion problem: Some workers in construction will privately add more water for a more fluid concrete. However, this will result in an increase in water-cement, resulting to a hardening of concrete strength that is insufficient, and the cracking phenomenon.
2. Transport and mixing issues: If mixing and transporting concrete takes too much time, the water in the concrete will evaporate quickly. concrete . This leads to a concrete that is weaker on the construction site, unable to meet construction specifications.
3. Construction speed
4. Maintenance is unreasonable. During the period of maintenance, if late watering isn't maintained, the result will be the Cracking phenomenon Later in the year, concrete will be used. Concrete is used in the future. Concrete Surface Watering You can water the concrete often to speed up the drying process. Concrete will shrink if it is not watered. Late cracking occurs when concrete strength is decreased.
5. Environmental factors: If the environment at the construction site is relatively dry and there is high temperature, wind, or both, then the evaporation rates of the concrete are accelerated. This results in cracking on the surface. Concrete constructions are most likely to crack in the winter or summer because of the temperature difference.
Solution: Add an agent to prevent cracking. A variety of inorganic composite materials can prevent over 80% of foam concrete from cracking. Add 2-3 kilograms of anti-cracking material per cubic meter.
Inquiry us
PREVIOUS NEWS
NEXT NEWS
It is very easy to cause concrete cracking if the construction or maintenance are not done correctly. What are then the five main causes of cracking concrete? 1. The cement proportion problem: Some workers in construction will privately add more wate…
Description of Molybdenum diulfide Molybdenum disulfide (also known as MoS2) is a transition metal sulfide. It is dark grey, or black solid. It has a layering crystal structure consisting of alternate arrangements of molybdenum- and sulfur-atoms. M…
Boron carburide is a high-performance carbon compound, which is composed primarily of boron, carbon, and other elements. The chemical formula for B4C is B4C. It is used widely in the aerospace and military industries for its hardness and melting poin…