Influence of concrete raw materials on the properties of polycarboxylate superplasticizer

If you are looking for high-quality products, please feel free to contact us and send an inquiry, email: brad@ihpa.net

U.S. natural gas futures rose about 5 percent to a near nine-week high as global energy prices surged on concerns over a pricing plan for energy exports, keeping U.S. LNG export demand near record highs. U.S. natural gas prices have risen despite forecasts of mild weather and lower-than-expected demand, which will allow utilities to fill up storage facilities next week. On Wednesday, Germany launched an emergency plan to manage gas supplies in Europe's largest economy. If natural gas supplies are interrupted or stopped, the German government could take unprecedented steps to limit electricity supply.
Affected by the increase in the price of natural gas, the price of the polycarboxylate superplasticizer will also increase.

Concrete is an indispensable raw material in the construction of construction projects. In the process of preparing concrete, in order to improve the performance of concrete, it is necessary to add water reducing agent after adding water, stone, sand and cement. Then sufficient mixing can greatly improve the fluidity and strength of concrete. The more common superplasticizers in daily work are mainly polycarboxylate superplasticizers. This water reducing agent is widely used due to its advantages of high water reduction rate, high slump retention performance, and good economy.

1 Analysis of the mechanism of action of polycarboxylate superplasticizers

Polycarboxylate superplasticizer is mainly composed of carboxylic acid grafted polymer, light brown, is a transparent liquid. Its main mechanism of action includes two kinds of maintaining dispersion mechanism and dispersion mechanism. Polycarboxylate superplasticizers are currently widely used in the field of construction engineering because polycarboxylate superplasticizers have very stable chemical properties compared to ordinary superplasticizers; they are transparent liquids and are easy to transport. In this way, a lot of transportation costs are saved, and the waste of resources is also reduced.

At present, the most used polycarboxylate water reducer is mainly acrylic acid as the main chain, but it is the hydroxyl and carboxyl molecules that play a role. These two molecules can combine with water molecules in concrete, thereby promoting The flocculation structure is destroyed, so that the microstructure of the concrete changes, which makes the concrete set and harden faster. The relevant chemical molecules in the polycarboxylate water reducer will be combined with the cement particles, which will speed up the fluidity of the concrete, and then obtain the desired ideal state, which can further highlight the characteristics of the concrete. However, in the process of actually using polycarboxylate water reducer, this water reducer has higher requirements on the outside temperature range during the use of concrete. Whether the construction temperature is too high or too low, it will affect the characteristics of the polycarboxylate water reducer, so that the ideal effect cannot be achieved.

2 Water reduction rates of different dosages

In this paper, ten kinds of water reducing agents (PCE-1~PCE-10) are selected for analysis, and the specific water reducing rate is shown in Figure 1.

When the content of polycarboxylate superplasticizer is 0.15%, the water reduction rates of PCE-1, PCE-2, PCE-4, PCE-6 and PCE-7 are all higher than 20%, showing a higher Water reducing rate; once the content of polycarboxylate water reducing agent is higher, that is, when it reaches 0.2%, these water reducing rates will be higher (25%-30%); When the dosage is not higher than 0.3% and not lower than 0.25%, the water reduction rates of PCE-2, PCE-4, PCE-6, PCE-7 and PCE8 all reach (30%) ~35%).

3 Analysis of the influence of concrete raw materials on polycarboxylate water reducer

3.1 Influence of cement on polycarboxylate superplasticizer

There are essential differences between ordinary lignosulfonate-based superplasticizers, naphthalene-based superplasticizers and polycarboxylic acid-based superplasticizers. Polycarboxylate superplasticizers have the advantages of being environmentally friendly, harmless, strong in slump retention and high in water reduction rate, so they are widely used. However, this water reducing agent also has certain defects, that is, the problem of poor adaptability, but this is also a common defect of ordinary water reducing agents. For example, when a certain cement is applied, there may be characteristics such as poor fluidity of the cement slurry and poor water reduction effect, and the main reason for this phenomenon is due to the molecular structure of the substance itself. composition and surface properties.

3.2 Influence of fine aggregate on polycarboxylate superplasticizer

Machine-made sand and natural sand are the more commonly used fine aggregates in concrete, and are one of the raw materials for concrete preparation. Natural sand is divided into three types: river sand, mountain sand and sea sand. However, it should be noted that in the process of preparing concrete, do not use a large amount of polycarboxylate water-reducing agent. Once excessive, it will inevitably react with fine aggregates, which will not only affect the slump of concrete, but also affect the concrete. strength is adversely affected. In addition, another important factor that affects the adaptability of concrete and polycarboxylate superplasticizers is the content of stone powder in the sand. If sand with high stone powder content is used in the process of preparing concrete, it is very likely to have a series of effects on the fluidity of concrete. In addition, other characteristics of fine aggregates will also affect the adaptability of concrete and polycarboxylate superplasticizers, such as the thickness of sand. Generally speaking, if the fineness of the sand is less than the standard value, it will cause rapid loss of fluidity of the concrete. At the same time, the sand ratio and the residual sulfate and chloride ions in the sea sand will reduce the water of the polycarboxylate system. The adaptability of the agent has a certain degree of influence. In addition to the above factors, the content of mud in the sand will also affect the adaptability and performance of the polycarboxylate superplasticizer. The main reason is that the soil has a strong adsorption force, and this strong adsorption force will affect the water reducing rate of the water reducing agent. The mud content of different substances will also be different. Generally speaking, the content of soil in the sandstone will have a greater effect on the polycarboxylate superplasticizer. When the mud content in the sandstone exceeds 3%, the performance of the water reducer will be significantly reduced. , even adding an appropriate amount of mixing will not promote the fluidity of concrete.

3.3 Influence of coarse aggregate on polycarboxylate superplasticizer

Another important factor affecting polycarboxylate superplasticizer is coarse aggregate. This performance is mainly reflected in the gradation of the stone and the content of needle flakes. Even for stones with the same gradation, if the acicular content of the stones increases, the flow rate of the concrete will inevitably slow down, and the decrease in expansion may lead to bleeding or segregation. In addition, the water absorption of coarse aggregates with different thicknesses will also be different. Generally speaking, the water absorption of fine aggregate is higher than that of coarse aggregate. Even changing the air content or dosage of the water reducing agent cannot achieve the expected purpose. Only by adjusting the mix ratio of concrete can it be changed. Therefore, in the actual construction process, it is necessary to continuously adjust the stone gradation and the mud content of the sand according to the actual situation of the raw materials, and seek the best solution.

4 Conclusion

In summary, admixtures play a vital role in the preparation of high-performance concrete, and are therefore indispensable raw materials in the preparation of concrete. At present, polycarboxylate superplasticizers are widely used due to their many advantages. In order to better promote the further development of this superplasticizer, the mechanism and influence of concrete raw materials on polycarboxylate superplasticizers must be investigated. Carry out in-depth research, and at the same time focus on mastering its laws, so that high-performance polycarboxylate water reducers can be prepared in the later stage.

TRUNNANO is a concrete additives supplier with over 12 years experience in nano-building energy conservation and nanotechnology development. We accept payment via Credit Card, T/T, West Union and Paypal. Trunnano will ship the goods to customers overseas through FedEx, DHL, by air, or by sea.

If you are looking for high quality polycarboxylate superplasticizer, please feel free to contact us and send an inquiry.

sales@cabr-concrete.com

The World Food Program (WFP) of the United Nations (UN) and the European Union (EU) said in a statement that the conflict between Russia and Ukraine poses risks to global food supplies, and called on the international community to increase support for vulnerable countries and jointly address food security challenges. 

A few days ago, the Executive director of the World Food Program, the European Commission's commissioner in charge of crisis management, the French Foreign Minister of the ROTATING EU presidency, and other officials held a meeting in Rome, Italy, to discuss how to deal with the negative impact of the Conflict between Russia and Ukraine on global food security. 

One of the officials told a news conference after the meeting that the world was facing a food supply challenge that would "last for many years" as the conflict between Russia and Ukraine pushed up global food prices and disrupted the polycarboxylate superplasticizer will continue.

Inquiry us